Titel

A liquid-like multiwalled carbon nanotube derivative and its epoxy nanocomposites

Ist Teil von

• Journal of applied polymer science, 2013-11, Vol.130 (3), p.2217-2224

Ort / Verlag

Hoboken, NJ: Blackwell Publishing Ltd

Erscheinungsjahr

2013

Link zum Volltext

Quelle

Wiley Online Library - AutoHoldings Journals

Beschreibungen/Notizen

• ABSTRACT Multiwall carbon nanotubes (MWCNTs) with liquid‐like behavior at room temperature were prepared with sulfonic acid terminated organosilanes as corona and tertiary amine as canopy. The liquid‐like MWCNT derivative had low viscosity at room temperature (3.89 Pa s at 20°C) and exhibited non‐Newtonian shear‐thinning behavior. The weight fraction of MWCNT in the derivative was 16.72%. The MWCNT derivative showed very good dispersion in organic solvents, such as ethanol and acetone. The liquid‐like MWCNT derivative was incorporated into epoxy matrix to investigate the mechanical performance of the nanocomposites and the distribution of MWCNTs in the matrix. When the liquid‐like MWCNT derivative content was up to 1 wt %, the flexural strength and impact toughness of composites were 12.1 and 124% higher than the pure epoxy matrix, respectively. Transmission electron microscope (TEM) confirmed the very good dispersion of the liquid‐like MWCNT derivative in epoxy matrix. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 130: 2217–2224, 2013