Comparison fabrication, identification and avoidance of corrosion potential of M-CuO NPs/S-CuO NPs to suppress corrosion on steel in an acidic solution

Ist Teil von

• Chemical papers, 2023-09, Vol.77 (9), p.5395-5407

Ort / Verlag

Cham: Springer International Publishing

Erscheinungsjahr

2023

Link zum Volltext

Quelle

SpringerLink (Online service)

Beschreibungen/Notizen

• The utilization of plants to produce metal oxide nanoparticles has recently received a lot of attention due to its ease of usage and environmental friendliness. Therefore, the aim of this study was to synthesize CuO NPs using two distinct methods, including an aqueous extract of moringa oleifera leaves (M-CuO NPs) and a synthetic approach (S-CuO NPs). Nanoparticles produced were evaluated by SEM, EDX, TEM and XRD, to consider the creation of CuO NPs and to determine the morphological, elemental constitution and size the samples. The average particles size 14.95 and 35.73 nm for S-CuO and M-CuO NPs, respectively, is having potentials for application as inhibitor in corrosion of MS. The inhibition and adsorption properties of prepared M-CuO NPs and S-CuO NPs on MS in 1 M HCl were investigated using the wt reduction assessment. The maximal IE of prepared M-CuO NPs and S-CuO NPs was 95.06% and 92.10%, respectively, at 1000 ppm. The IE % improves with greater concentration of the prepared M-CuO NPs and S-CuO NPs. According to the findings, M-CuO NPs are the most effective green potential inhibitor for MS in acidic conditions. It is demonstrated that the Langmuir isotherms are obeyed by the produced CuO NPs and MS substrate.