Details

Autor(en) / Beteiligte

• Wang, Yixiong
• Zhou, Chungen

Titel

Hot corrosion behavior of nanostructured Gd2O3 doped YSZ thermal barrier coating in presence of Na2SO4 + V2O5 molten salts

Ist Teil von

• Progress in natural science, 2017-08, Vol.27 (4), p.507-513

Ort / Verlag

Elsevier B.V

Erscheinungsjahr

2017

Quelle

Alma/SFX Local Collection

Beschreibungen/Notizen

• Nickel-based superalloy DZ125 was first sprayed with a NiCrAlY bond coat and followed with a nanostructured 2mol% Gd2O3−4.5mol% Y2O3-ZrO2 (2GdYSZ) topcoat using air plasma spraying (APS). Hot corrosion behavior of the as-sprayed thermal barrier coatings (TBCs) were investigated in the presence of 50wt% Na2SO4 + 50wt% V2O5 as the corrosive molten salt at 900°C for 100h. The analysis results indicate that Gd doped YVO4 and m-ZrO2 crystals were formed as corrosion products due to the reaction of the corrosive salts with stabilizers (Y2O3, Gd2O3) of zirconia. Cross-section morphology shows that a thin layer called TGO was formed at the bond coat/topcoat interface. After hot corrosion test, the proportion of m-ZrO2 phase in nanostructured 2GdYSZ coating is lower than that of nano-YSZ coating. The result reveals that nanostructured 2GdYSZ coating exhibits a better hot corrosion resistance than nano-YSZ coating.