• Yu, W.
• Azhdar, B.
• Andersson, D.
• Reitberger, T.
• Hassinen, J.
• Hjertberg, T.
• Gedde, U.W.

Titel

Deterioration of polyethylene pipes exposed to water containing chlorine dioxide

Ist Teil von

• Polymer degradation and stability, 2011-05, Vol.96 (5), p.790-797

Ort / Verlag

Kidlington: Elsevier Ltd

Erscheinungsjahr

2011

Quelle

Alma/SFX Local Collection

Beschreibungen/Notizen

• Chlorine species used as disinfectants in tap water have a deteriorating effect on many materials including polyethylene. There are only very few scientific reports on the effect on polyethylene pipes of water containing chlorine dioxide. Medium-density polyethylene pipes stabilized with hindered phenol and phosphite antioxidants were pressure tested with water containing 4 ppm chlorine dioxide at 90 °C and pH = 6.8 as internal medium. The stabilizers were rapidly consumed towards the inner pipe wall; the rate of consumption was four times greater than in chlorinated water (4 ppm, pH = 6.8) at the same temperature. The depletion of stabilizer occurred far into the pipe wall. A supplementary study on a polymer analogue (squalane) containing the same stabilizer package showed that the consumption of the phenolic antioxidant was 2.5 times faster when exposed water containing chlorine dioxide than on exposure to chlorinated water. The subsequent polymer degradation was an immediate surface reaction. It was confirmed by differential scanning calorimetry, infrared spectroscopy and size exclusion chromatography that in the surface layer which came into contact with the oxidising medium, the amorphous component of the polymer was heavily oxidized leaving a highly crystalline powder with many carboxylic acid chain ends in extended and once-folded chains. Scanning electron microscopy showed that propagation of cracks through the pipe wall was assisted by polymer degradation.