Effect of positively charged particles on sputtering damage of organic electro-luminescent diodes with Mg:Ag alloy electrodes fabricated by facing target sputtering

Ist Teil von

• AIP advances, 2017-04, Vol.7 (4), p.045014-045014-8

Ort / Verlag

AIP Publishing LLC

Erscheinungsjahr

2017

Quelle

EZB Free E-Journals

Beschreibungen/Notizen

• We investigated the influence of the positively charged particles generated during sputtering on the performances of organic light-emitting diodes (OLEDs) with Mg:Ag alloy electrodes fabricated by sputtering. The number of positively charged particles increased by several orders of magnitude when the target current was increased from 0.1 A to 2.5 A. When a high target current was used, many positively charged particles with energies higher than the bond energy of single C–C bonds, which are typically found in organic molecules, were generated. In this situation, we observed serious OLED performance degradation. On the other hand, when a low target current was used, OLED performance degradation was not observed when the number of positively charged particles colliding with the organic underlayer increased. We concluded that sputtering damage caused by positively charged particles can be avoided by using a low target current.