Development of TiO 2 /ZrO 2 Multi-Material Obtained from Ceramic Pastes for Material Extrusion
Ist Teil von
Micromachines (Basel), 2023-11, Vol.14 (12)
Ort / Verlag
Switzerland
Erscheinungsjahr
2023
Link zum Volltext
Quelle
EZB Free E-Journals
Beschreibungen/Notizen
The application of additive manufacturing method such as material extrusion (MEX) allows the successful fabrication of ceramic products, including multi-ceramic products. Promising materials in this research area are TiO
and ZrO
ceramics, which can be used in electrical and electronic engineering. The aim of this work is to investigate the possibility of fabricating TiO
/ZrO
multi-materials from ceramic pastes that can be used in the MEX. In this work, defects, chemical and phase composition, and microhardness were analyzed in multi-ceramic samples after sintering. Multi-ceramic TiO
/ZrO
samples after the sintering process without interlayer could not be fabricated due to a too large difference in shrinkage between TiO
and ZrO
. The samples with one and three interlayers also have defects, but they are less significant and can be fabricated. The average hardness for the TiO
zone was 636.7 HV and for the ZrO
zone was 1101 HV. In the TiO
zone, only TiO
phase in rutile is observed, while in the interlayer zones, in addition to rutile, ZrO
and ZrTiO
are also present, as is a small amount of Y
O
. In the zone ZrO
, only the ZrO
phase is observed. The chemical analysis revealed that the interlayers comprise sintered ZrO
granules enveloped by TiO
, ZrO
, and ZrTiO
.
Sprache
Englisch
Identifikatoren
ISSN: 2072-666X
eISSN: 2072-666X
Titel-ID: cdi_pubmed_primary_38138346
Format
–
Weiterführende Literatur
Empfehlungen zum selben Thema automatisch vorgeschlagen von bX