Multiple denaturational transitions in fibrillar collagen

Ist Teil von

• Biopolymers, 1986-10, Vol.25 (10), p.1875-1893

Ort / Verlag

Hoboken: Wiley Subscription Services, Inc., A Wiley Company

Erscheinungsjahr

1986

Link zum Volltext

Quelle

MEDLINE

Beschreibungen/Notizen

• The heat denaturation of pepsinized bovine nonfibrillar and fibrillar collagen was studied by differential scanning calorimetry. For fibrillar preparations that had been rapidly precipitated with stirring at low ionic strength, then resuspended at physiological ionic strength, multiple denaturational transitions were observed. At heating rates of 10°C/min, melting endotherms occurred at about 44, 50, 53, and 57°C. Fibrillar collagen that was slowly gelled without stirring at physiological ionic strength exhibited a similar series of endotherms, but the lower melting transitions were less conspicuous. In contrast, nonfibrillar bovine collagen in acidic solution showed only a single denaturational transition at 40°C. Nonfibrillar solutions at pH 7, to which inhibitors of fibrillogenesis were added, showed a major endotherm as high as 46°C. These results suggest that reconstituted fibrillar collagen contains a heterogeneous fibril population, possibly including molecules in a nonfibrillar state. It was proposed that the multiple melting endotherms of such preparations were due to sequential melting of molecular and fibril classes, each with a distinct melting temperature. The fibrillar classes may represent three or more types of banded and nonbanded species that differ from each other in packing order, collagen concentration, and possibly also in fibril width and level of cross‐linking.