The discontinuous precipitation of a high-nitrogen (0.8 wt%) austenitic steel has been investigated after successive steps of heat treatment at two different temperatures (800 and 850 °C). After each step of heating the material has been examined by X-ray diffraction (XRD), optical microscopy (OM), transmission electron microscopy (TEM), Auger electron spectroscopy (AES) and microhardness tests. The precipitation of Cr2N induces the formation of a secondary austenitic phase, leads to the redistribution of N between transformed and untransformed zones and to local variations of mechanical properties.
Sprache
Englisch
Identifikatoren
ISSN: 0255-5476, 1662-9752
eISSN: 1662-9752
DOI: 10.4028/www.scientific.net/MSF.638-642.3597
Titel-ID: cdi_proquest_miscellaneous_743174708
Format
–
Weiterführende Literatur
Empfehlungen zum selben Thema automatisch vorgeschlagen von bX