Titel

High-Temperature Anodized WO3 Nanoplatelet Films for Photosensitive Devices

Ist Teil von

• Langmuir, 2009-08, Vol.25 (16), p.9545-9551

Ort / Verlag

United States: American Chemical Society

Erscheinungsjahr

2009

Quelle

Alma/SFX Local Collection

Beschreibungen/Notizen

• Anodization at elevated temperatures in nitric acid has been used for the production of highly porous and thick tungsten trioxide nanostructured films for photosensitive device applications. The anodization process resulted in platelet crystals with thicknesses of 20−60 nm and lengths of 100−1000 nm. Maximum thicknesses of ∼2.4 μm were obtained after 4 h of anodization at 20 V. X-ray diffraction analysis revealed that the as-prepared anodized samples contain predominantly hydrated tungstite phases depending on voltage, while films annealed at 400 °C for 4 h are predominantly orthorhombic WO3 phase. Photocurrent measurements revealed that the current density of the 2.4 μm nanostructured anodized film was 6 times larger than the nonanodized films. Dye-sensitized solar cells developed using these films produced 0.33 V and 0.65 mA/cm2 in open- and short-circuit conditions.