Details

Autor(en) / Beteiligte

• Zhang, Xuan
• Steckler, Timothy T.
• Dasari, Raghunath R.
• Ohira, Shino
• Potscavage, William J.
• Tiwari, Shree Prakash
• Coppée, Séverine
• Ellinger, Stefan
• Barlow, Stephen
• Brédas, Jean-Luc
• Kippelen, Bernard
• Reynolds, John R.
• Marder, Seth R.

Titel

Dithienopyrrole-based donor–acceptor copolymers: low band-gap materials for charge transport, photovoltaics and electrochromism

Ist Teil von

• Journal of materials chemistry, 2010, Vol.20 (1), p.123-134

Erscheinungsjahr

2010

Quelle

Alma/SFX Local Collection

Beschreibungen/Notizen

• A series of highly soluble donor-acceptor (D-A) copolymers containing N-(3,4,5-tri-n-decyloxyhenyl)-dithieno[3,2-b:2',3'-d]pyrrole (DTP) or N-(2-decyltetradecyl)-dithieno[3,2-b:2',3'-d]pyrrole (DTP) as donor and three different acceptors, 4,7-dithien-2-yl-[2,1,3]-benzothiadiazole, 4,9-dithien-2-yl-6,7-di-nhexyl-[1,2,5]thiadiazolo[3,4-g]quinoxaline and 4,8-dithien-2-yl-2l(4)d(2)-benzo[1,2-c;4,5-c']bis[1,2,5]thiadiazole (BThX,X = BTD, TQHx(2), BBT, respectively) were synthesized by Stille coupling polymerizations. The optical and electrochemical properties of these copolymers were investigated, along with their use in field-effect transistors and photovoltaic devices. The band gaps (eV) estimated from UV-vis-NIR spectra and electrochemical measurements of the copolymers varied from ca. 1.5-0.5 eV, and were consistent with quantum-chemical estimates extrapolated using density functional theory. Oxidative and reductive spectroelectrochemistry of the copolymers indicated they can be be both p-doped and n-doped, and three to four differently colored redox states of the polymers can be accessesd through electrochemical oxidation or reduction. The DTP-BThBTD and DTP-BThTQHx(2) copolymers exhibited average field-effect hole mobilities of 1.2 x 10(-4) and 2.2 x 10(-3) cm(2)/(Vs), respectively. DTP-BThBBT exhibited ambipolar field-effect characteristics and showed hole and electron nobilities of 1.2 x 10(-3) and 5.8 x 10(-4) cm(2)/(Vs), respectively. Bulk heterojunction photovoltaic devices made from blends of the copolymers with 3'-phenyl-3' H-cyclopropa[1,9](C(60)-I(h)[5,6]fullerene-3'-butanoic acid methyl ester (PCBM) (1:3 weight ratio) exhibited average power conversion efficiencies as high as 1.3% under simulated irradiance of 75 mW/cm(2).