Titel

Ag Single Atoms Anchored on CeO2 with Interfacial Oxygen Vacancies for Efficient CO2 Electroreduction

Ist Teil von

• ACS applied materials & interfaces, 2023-06, Vol.15 (25), p.30262-30271

Ort / Verlag

American Chemical Society

Erscheinungsjahr

2023

Quelle

Alma/SFX Local Collection

Beschreibungen/Notizen

• Ag single-atom catalysts (SACs) have great potential in selective electrocatalysis of the CO2 reduction reaction (CO2RR) to CO, while it is still a challenge to achieve high current density and high atom efficiency simultaneously. Here, we present a new and simple in situ adsorption–reduction method to prepare Ag SACs supported on CeO2 (Ag1/CeO2). It is found that Ag single atoms are anchored on CeO2 through strong metal–support interaction (SMSI), and each Ag atom is accompanied with three interfacial oxygen vacancies. This Ag1/CeO2 exhibits high performance in the electrocatalytic CO2RR with a high CO faradaic efficiency (FE) of >95% under a wide potential range. The turnover frequency (TOF) value can reach 50,310 h–1 at FECO = 99.5% in H-cells. Notably, Ag1/CeO2 achieves an industrial-grade current density of 403 mA cm–2 with a high FECO of 97.2% in flow cells. Experimental results combined with density functional theory calculation revealed that this superior performance was mainly ascribed to the existence of interfacial oxygen vacancies, which lead to the formation of Ag–O–Ce3+ atomic interfaces, and activates the Ce3+–O structures as the synergistic active center of Ag, thus promoting CO2 adsorption and activation and reducing the reaction potential barrier of *COOH-to-*CO.