Strategy of Solution-Processed All-Inorganic Heterostructure for Humidity/Temperature-Stable Perovskite Quantum Dot Light-Emitting Diodes
Ist Teil von
ACS nano, 2018-02, Vol.12 (2), p.1462-1472
Ort / Verlag
United States: American Chemical Society
Erscheinungsjahr
2018
Quelle
Alma/SFX Local Collection
Beschreibungen/Notizen
Recently, a pressing requirement of solid-state lighting sources with high performance and low cost has motivated increasing research in metal halide perovskites. However, the relatively low emission efficiency and poor operation stability of perovskite light-emitting diodes (LEDs) are still critical drawbacks. In this study, a strategy of solution-processed all-inorganic heterostructure was proposed to overcome the emission efficiency and operation stability issues facing the challenges of perovskite LEDs. Solution-processed n-ZnO nanoparticles and p-NiO are used as the carrier injectors to fabricate all-inorganic heterostructured CsPbBr3 quantum dot LEDs, and a high-efficiency green emission is achieved with maximum luminance of 6093.2 cd/m2, external quantum efficiency of 3.79%, and current efficiency of 7.96 cd/A. More importantly, the studied perovskite LEDs possess a good operation stability after a long test time in air ambient. Typically, the devices can endure a high humidity (75%, 12 h) and a high working temperature (393 K, three heating/cooling cycles) even without encapsulation, and the operation stability is better than any previous reports. It is anticipated that this work will provide an effective strategy for the fabrication of high-performance perovskite LEDs with good stability under ambient and harsh conditions, making practical applications of such LEDs a real possibility.
Sprache
Englisch
Identifikatoren
ISSN: 1936-0851
eISSN: 1936-086X
DOI: 10.1021/acsnano.7b07856
Titel-ID: cdi_proquest_miscellaneous_1989575233
Format
–
Weiterführende Literatur
Empfehlungen zum selben Thema automatisch vorgeschlagen von bX