Titel

Rational Design of Solution-Processed Ti–Fe–O Ternary Oxides for Efficient Planar CH3NH3PbI3 Perovskite Solar Cells with Suppressed Hysteresis

Ist Teil von

• ACS applied materials & interfaces, 2017-10, Vol.9 (40), p.34833-34843

Ort / Verlag

American Chemical Society

Erscheinungsjahr

2017

Link zum Volltext

Quelle

Alma/SFX Local Collection

Beschreibungen/Notizen

• Electron-extraction layer (EEL) plays a critical role in determining the charge extraction and the power conversion efficiencies of the organometal-halide perovskite solar cells (PSCs). In this work, Ti–Fe–O ternary oxides were first developed to work as an efficient EEL in planar PSC. Compared with the widely used TiO x and the pure FeO x , the ternary composites show superior properties in multiple aspects including the excellent stability of the precursor solution, good coverage on the substrates, outstanding electrical properties, and suitable energy levels. By varying the Fe content from 0 to 100% in the Ti–Fe–O composites, the conductivity of the resultant compact layer was markedly improved, confirmed by consistent results from the conductive atomic force microscopy and the linear sweep voltammetry measurements. Meanwhile, the compositional engineering tunes the energy level alignment of the Ti–Fe–O EEL/CH3NH3PbI3 interface to a region that is favorable for obtaining excellent charge-extraction property. The combinational advantages of the Ti–Fe–O composites significantly improved the photovoltaic performance of the as-prepared solar cells. An increase of over 20% in the short-circuit current (J SC) density has been achieved due to a modified EEL conductivity and energy alignment with the perovskite layer. The reduction in the surface recombination and enhancement of the charge collection efficiency also result in about 15% increase in the fill factor. Notably, the device also showed remarkably alleviated hysteresis behavior, revealing a prominently inhibited surface recombination.