Titel

In-situ imidization analysis in microscale thin films of an ester-type photosensitive polyimide for microelectronic packaging applications

Ist Teil von

• European polymer journal, 2016-11, Vol.84, p.279-291

Ort / Verlag

Oxford: Elsevier Ltd

Erscheinungsjahr

2016

Quelle

Alma/SFX Local Collection

Beschreibungen/Notizen

• [Display omitted] •Crosslinked ester groups shift the PI conversion function to higher temperatures.•Above a certain crosslinking density the achievable degree of imidization is limited to 95%.•UV exposure dose should be set below a certain threshold to achieve full imidization.•Film shrinkage measurements by TEA is an excellent indicator to follow the imidization in thin films. The imidization reaction in thin films of an ester-type photosensitive polyimide is investigated in the temperature range of 50–450°C by temperature dependent rapid-scan in-situ FT-IR spectroscopy, thermo-ellipsometric analysis and thermogravimetric analysis coupled with evolved gas analysis. The influence of the UV crosslinkable methacrylic functional group in the polymer sidechain on the imidization reaction is studied. For non-crosslinked precursor films the imidization is completed at ≈250°C. Depending on the amount of crosslinking the temperature to achieve full imidization is shifted to higher values. Above a certain amount of crosslinking the degree of imidization is limited to ≈95% for temperatures below 280°C. The reaction continues by further increase of the temperature to >340°C. Evolved gas analyses indicate that the cleave-out of crosslinker is required to finish the imidization. The film shrinkage and weight loss is correlated to the degree of imidization.