Effect of strain rate on the mechanical properties of magnesium alloy AMX602
Ist Teil von
Materials science & engineering. A, Structural materials : properties, microstructure and processing, 2016-01, Vol.649, p.338-348
Ort / Verlag
Elsevier B.V
Erscheinungsjahr
2016
Quelle
Alma/SFX Local Collection
Beschreibungen/Notizen
In the present work, the effect of strain rate on the mechanical properties, particularly the plastic deformation behavior of a magnesium alloy, AMX602 (Mg–6%Al–0.5%Mn–2%Ca; all wt%), fabricated by powder metallurgy, has been investigated under both quasi-static (strain rate 1×10−3s−1) and dynamic (strain rate 4×103s−1) compressive loading. The alloyed powder was extruded at three different temperatures. The microstructure of the alloy was examined by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). It was found that AMX602 exhibits an impressive mechanical behavior but with a slight anisotropy along different directions in both strength and compressive ductility (or malleability). The strength was found to be nearly independent of the extrusion temperature, particularly, under dynamic loading. Nanoindentation strain rate jump test reveals a strain rate sensitivity of ~0.018 to ~0.015, depending on the extrusion temperature. Sub-micrometer-scale particles of the intermetallic compound Al2Ca were found with sizes ranging from ~100nm to ~1.0μm. These intermetallic particles are believed to have precipitated out during the extrusion process. They contribute to the formation of the ultrafine equiaxed grains which, in turn, help to improve the strength of the alloy by acting as barriers to dislocation motion. Adiabatic shear bands (ASBs) were observed in the dynamically loaded samples, the propagation of which eventually leads to final fracture of the specimens.