Preparation and characterization of sol-gel derived high lithium ion conductive NZP-type ceramics Li sub(1 + x)Al sub(x)Ti sub(2 - x)(PO sub(4)) sub(3)

Ist Teil von

• Solid state ionics, 2015-06, Vol.274, p.77-82

Erscheinungsjahr

2015

Quelle

Alma/SFX Local Collection

Beschreibungen/Notizen

• Solid electrolytes based on lithium titanium aluminum phosphate (LATP) with the composition Li sub(1.3)Al sub(0.3)Ti sub(1.7)(PO sub(4)) sub(3) were prepared employing a modified sol-gel method. Amorphous LATP was converted to a ceramic by a heat treatment at 900 [degrees]C. Densification was achieved by field assisted sintering (FAST) in the temperature range of 850 to 1100 [degrees]C. The resulting phase composition, crystal structure and theoretical density were obtained from XRD analysis. Electrical properties of the samples, such as ionic conductivity, were calculated from impedance measurements in the frequency range from 20 Hz to 1 MHz. The ionic conductivities of the sintered pellets were calculated from impedance data and were correlated with the sample density. A maximum conductivity in the order of 10 super(-3) S cm super(-1) at room temperature is obtained for phase-pure compositions combined with a high relative density of 98%.