Study on titania nanotube arrays prepared by titanium anodization in NH sub(4)F/H sub(2)SO sub(4) solution
Ist Teil von
Journal of materials science, 2007-07, Vol.42 (14), p.5539-5543
Erscheinungsjahr
2007
Link zum Volltext
Quelle
SpringerNature Journals
Beschreibungen/Notizen
In this paper, the formation of titania nanotube arrays was investigated in NH sub(4)F/H sub(2)SO sub(4) electrolyte. Under optimized electrolyte conditions, the titania nanotube arrays with an inner diameter of about 120 nm and a length of about 300 nm was obtained. During the formation process, the variety of current was observed. The current-time curve implied that the evolvement process of titania nanotube arrays include three stages. The stability of titania nanotube arrays at elevated temperatures was studied. The as-prepared titania nanotube arrays is amorphous, crystallized in anatase and rutile as the rising of the temperature. The samples were characterized by ESEM and XRD.