• Sun, Lu
• Guo, Junsong
• Zhou, Jie
• Xu, Qingming
• Chu, Deryn
• Chen, Rongrong

Titel

Novel nanostructured high-performance anion exchange ionomers for anion exchange membrane fuel cells

Ist Teil von

• Journal of power sources, 2012-03, Vol.202, p.70-77

Ort / Verlag

Amsterdam: Elsevier B.V

Erscheinungsjahr

2012

Quelle

Access via ScienceDirect (Elsevier)

Beschreibungen/Notizen

• [Display omitted] ► Nanostructured triblock SEBS-based ionomers were demonstrated to have excellent dimensional stability against hydration, without significantly sacrificing the ionic conductivity, as compared to a polysulfone(PSf)-based ionomer. ► The fuel cell and impedance test results indicated a significant performance advantage of the SEBS-based ionomers over the PSf-based ionomer. ► AFM phase imaging and electrochemical impedance spectroscopy were demonstrated to be very useful techniques to study structures and performance of ionomers. A novel block copolymer, styrene–ethylene/butylene–styrene (SEBS), was chosen as the starting material to prepare pendant quaternary ammonium-based ionomers with an ion-exchange-capacity (IEC) of 0.66, 1.30, and 1.54 mequiv. g −1, denoted by QSEBS-L, QSEBS-M, and QSEBS-H, respectively. These QSEBS ionomers have been demonstrated to have excellent dimensional stability against hydration without significantly sacrificing the ionic conductivity as compared to the widely studied polysulfone (PSf)-based ionomers. The water uptake of the QSEBS-based ionomers depended on their functionality; a higher IEC in the ionomer resulted in more water uptake and a higher ionic conductivity. The MEAs fabricated with the QSEBS-M and QSEBS-H ionomers showed the best H 2/O 2 fuel cell performance with peak power densities reaching 210 mW cm −2 at 50 °C, which was significantly higher than that of the PSf-based ionomers (∼30 mW cm −2). Electrochemical impedance spectroscopy (EIS) analysis indicated that the superior fuel cell performance observed with the QSEBS-based ionomers can be attributed to: (1) the low internal cell resistance, and (2) the low charge transfer resistance in both the anode and the cathode due to the excellent dimensional stability and the balanced conductivity-hydrophobicity originated by the unique morphology of the QSEBS-based ionomers. AFM phase imaging measurements of the QSEBS-based ionomers revealed unique nanostructures containing isolated hydrophobic and continuous anion conducting hydrophilic domains. By further optimizing the chemistry and morphology of the ionomers and the membranes, the resistance of the anode and cathode of the AEMFCs will be further reduced. The performance of anion-exchange-membrane fuel cells will be further improved.