• Liu, Yumeng
• Zhang, Jinniu
• Li, Gang
• Liu, Jia
• Liang, Qingfei
• Wang, Hongjun
• Zhu, Yuanyuan
• Gao, Jianzhi
• Lu, Hongbing

Titel

In2O3–ZnO nanotubes for the sensitive and selective detection of ppb-level NO2 under UV irradiation at room temperature

Ist Teil von

• Sensors and actuators. B, Chemical, 2022-03, Vol.355, p.131322, Article 131322

Ort / Verlag

Lausanne: Elsevier B.V

Erscheinungsjahr

2022

Link zum Volltext

Quelle

Alma/SFX Local Collection

Beschreibungen/Notizen

• In2O3–ZnO nanotubes were prepared by a solvent thermal method using electrospun indium nitrate–polyvinyl pyrrolidone [In(NO3)3–PVP] nanofibers as a sacrificial template. The sensing properties toward NO2 of this kind of new emerging sensing material were explored. Compared with as-electrospun In2O3 nanofibers, the In2O3–ZnO composite nanotubes exhibited higher responses and better selectivity to NO2. The response of the In2O3–ZnO nanotubes to 500 ppb NO2 at room temperature (RT, 25 °C) under UV irradiation was as high as to 32.73, which was 3.33 times higher than that of the In2O3 nanofibers. Moreover, even under a high relative humidity of 80%, the RT NO2 response of the In2O3–ZnO composite nanotubes can still reach up to 3.50–500 ppb. The enhanced NO2 sensing characteristics were mainly ascribed to the formation of In2O3–ZnO n–n heterojunctions, the enhanced light absorption, and the increased oxygen vacancy proportion. The results suggested that In2O3–ZnO nanotubes had good potential for the selective and sensitive detection of ppb-level NO2 at RT. [Display omitted] Highly sensitive and selective NO2 sensor for ppb-level detection under UV irradiation at room temperature was constructed using In2O3–ZnO nanotubes as sensing material. •In2O3–ZnO nanotubes were prepared by a solvothermal method.•In(NO3)3–PVP nanofibers were used as In source and sacrificial template.•In2O3–ZnO n–n heterojunctions were formed in the nanotubes.•The nanotubes exhibited sensitive and selective detection of ppb-level NO2 at RT.•The gas-sensing enhancement mechanism of In2O3–ZnO was proposed.