Experimental study of hot pressed sintered modified materials

Ist Teil von

• Journal of physics. Conference series, 2020-03, Vol.1507 (3), p.32061

Ort / Verlag

Bristol: IOP Publishing

Erscheinungsjahr

2020

Quelle

EZB Electronic Journals Library

Beschreibungen/Notizen

• The PTFE/Cu composite powder was selected as the experimental raw material, and the modified material PTFE/Cu with dense structure was prepared by hot pressing sintering process. The morphology of the product before and after the test was compared and observed by SEM. The effect of different material ratios on the densification results of the powder was studied, and the difference between molding and hot pressing sintering was analyzed. The results show that hot-pressed sintering can produce modified PTFE/Cu with a density of up to 99.9%, which is higher than that obtained by molding under the same pressure. The SEM image shows that, unlike the molding, hot-pressing sintering makes the crystal grains of the two materials exist independently in the modified polymer, and makes the powder crystal grains gradually perpendicular to the hot pressing direction.