• Khan, Muhammad Masood
• Jin, Lijun
• Khan, Muhammad Mahmood
• Li, Yang
• Saulat, Hammad
• Zhang, Yun
• Sarfraz, Muhammad
• Zhu, Jialong
• Hu, Haoquan

Titel

CO2 reforming of methane over activated carbon-Ni/MgO-Al2O3 composite catalysts for syngas production

Ist Teil von

• Fuel processing technology, 2021-01, Vol.211, p.106595, Article 106595

Ort / Verlag

Amsterdam: Elsevier B.V

Erscheinungsjahr

2021

Quelle

Access via ScienceDirect (Elsevier)

Beschreibungen/Notizen

• The composite catalysts AC-Ni/MgO-Al2O3 were prepared by the co-precipitation method with activated carbon (AC) and [Ni,Mg,Al]-hydrotalcite as the precursors, and characterized by XRD, TG-DTG, N2 adsorption, H2-TPR and SEM, respectively. The resultant catalysts were examined for CO2 reforming of methane. The results showed that the introduction of AC into Ni/MgO-Al2O3 catalyst improved the textural properties, especially the surface area and pore volume of mesopores, and decreased the size of metal Ni. Compared with Ni/MgO-Al2O3, the composite AC-Ni/MgO-Al2O3 exhibited higher catalytic activity, stability and H2/CO ratio. But the AC content obviously influenced the catalytic performances. High AC loading resulted in the decline of catalytic activity owing to lower surface area and fewer active Ni content in the catalyst. 10AC-Ni/MgO-Al2O3 with 10% AC displayed the best catalytic activity and stability compared with Ni/MgO-Al2O3. About 86.2% conversion of CH4, 91.3% conversion of CO2 and above 0.95 ratio of H2/CO were achieved over 10AC-Ni/MgO-Al2O3 sample for the reaction time of 5430 min. This work provides a route to improve catalytic performances of Ni-based catalysts in CO2 reforming of methane. •The AC-Ni/MgO-Al2O3 composite catalyst was prepared by co-precipitation method.•Activated carbon (AC) and [Ni, Mg, Al]-hydrotalcite were used as the precursors.•The AC addition into Ni/MgO-Al2O3 improves textural properties and reduces Ni size.•Catalytic activity, stability and H2/CO ratio are greatly improved on composite catalyst.•AC-Ni/MgO-Al2O3 with 10% AC displayed the best catalytic activity and stability.