Improvement of critical current density of MgB2 bulk superconductor processed by Spark Plasma Sintering

Ist Teil von

• Journal of the American Ceramic Society, 2020-11, Vol.103 (11), p.6169-6175

Ort / Verlag

Columbus: Wiley Subscription Services, Inc

Erscheinungsjahr

2020

Link zum Volltext

Quelle

Wiley Online Library Journals Frontfile Complete

Beschreibungen/Notizen

• Spark Plasma Sintering (SPS) is a promising rapid consolidation technique that allows a better understanding and optimization of the sintering kinetics and therefore makes it possible to obtain MgB2 bulk superconductor with tailored microstructures consisting of grains with either spherical or elongated morphology. In this contribution, the role of the precursor powders on the superconducting properties of MgB2 is investigated. Three sets of bulk MgB2 material were processed from: (i) a commercially available MgB2 powder; (ii) a mixture of Mg metal and amorphous B using a single‐step solid‐state reaction process and (iii) a mixture of amorphous boron coated with carbon and Mg metal. The samples were prepared in the same SPS processing conditions. The microstructure of the samples was investigated by X‐ray diffraction, SEM and TEM and correlated to their superconducting properties. The critical current density of the best sample at 20K was Jc = 500 kA/cm2 in self‐field, which is one of the highest critical current density reported for MgB2 bulk superconductors.