• Zhan, Zuo‐min
• Yan, Hong‐qiang
• Yin, Ping
• Cheng, Jie
• Fang, Zheng‐ping

Titel

Synthesis and properties of a novel bio‐based benzoxazine resin with excellent low‐temperature curing ability

Ist Teil von

• Polymer international, 2020-04, Vol.69 (4), p.355-362

Ort / Verlag

Chichester, UK: John Wiley & Sons, Ltd

Erscheinungsjahr

2020

Quelle

Wiley Online Library Journals Frontfile Complete

Beschreibungen/Notizen

• A novel bio‐based benzoxazine resin (diphenolic acid/furfurylamine benzoxazine resin, PDPA‐F‐Boz) was prepared by using bio‐based diphenolic acid, furfurylamine and paraformaldehyde as raw materials. The structure of DPA‐F‐Boz monomer was characterized by Fourier transform infrared spectroscopy, 1H NMR and 13C NMR, and then its curing reaction and the thermal stability of the cured PDPA‐F‐Boz were analyzed. Compared with the traditional fossil‐based benzoxazine (bisphenol A/aniline benzoxazine, BPA‐A‐Boz) and the bio‐based benzoxazine (diphenolic acid/aniline benzoxazine, DPA‐A‐Boz), DPA‐F‐Boz monomer showed the lowest curing temperature, and PDPA‐F‐Boz had the highest residual char ratio at 800 °C and the lowest degradation rate at the peak temperature. Meanwhile, the total heat release, peak heat release rate and heat release capacity of PDPA‐F‐Boz were much lower than those of PBPA‐A‐Boz and PDPA‐A‐Boz. Thus, PDPA‐F‐Boz showed excellent low‐temperature curing ability and thermal stability. © 2019 Society of Chemical Industry The bio‐based benzoxazine (diphenolic acid/furfurylamine benzoxazine, PDPA‐F‐Boz) had been synthesized and behaved as an excellent flame retardant bio‐based benzoxazine resin with low‐temperature curing ability and intrinsic thermal stability.