• Ding, Yue
• Feng, Wutong
• Huang, Dan
• Lu, Bo
• Wang, Pingli
• Wang, Gexia
• Ji, Junhui

Titel

Compatibilization of immiscible PLA-based biodegradable polymer blends using amphiphilic di-block copolymers

Ist Teil von

• European polymer journal, 2019-09, Vol.118, p.45-52

Ort / Verlag

Oxford: Elsevier Ltd

Erscheinungsjahr

2019

Quelle

Alma/SFX Local Collection

Beschreibungen/Notizen

• [Display omitted] •MPEG-PLA improved the compatibility of PLA-based blends.•MPEG-PLA improved the ductility of the PLA/PBAT blends (296% vs. 30%).•MPEG-PLA improved the interfacial adhesion of the blends. Block copolymer is an effective compatibilizer for PLA-based biodegradable polyester blends to improve the mechanical properties. However, how to find an “A-C” type of di-block copolymer as a common compatibilizer for improving the miscibility of A and B blends is very challenging. In this research, monomethoxy poly(ethylene glycol)-polylactide (MPEG-PLA) di-block copolymers were synthesized for compatibilization of PLA-based polyester blends, such as PLA with poly(butylene adipate-co-terephthalate) (PBAT), or poly(butylene succinate) (PBS), or poly(butylene succinate-co-adipate) (PBSA). The results showed that the di-block successfully reduced the interfacial tension and improved the interfacial adhesion, thereby, the size of dispersed phase decreased from 2 μm to 0.3 μm with the addition of MPEG-PLA copolymer which the segment ratio of EG/LA was 2.5 in PLA/PBAT blends. Moreover the elongation at the break of the blends was as high as 296%, which was ten times more than the pristine blends. Furthermore the MPEG-PLA di-block copolymer with specific structure improved the mechanical properties and changed the phase morphology of PLA/PBS and PLA/PBSA blends. In the blends, PEG segment in “A-C” di-block copolymer acted as B blocks in “A-B” di-block copolymers to improve the compatibility of PLA-based biodegradable polymer blends.