Influence of Coke Content on Sintering Process of Chromium-containing Vanadium-titanium Magnetite
Ist Teil von
Journal of Wuhan University of Technology. Materials science edition, 2018-02, Vol.33 (1), p.68-72
Ort / Verlag
Wuhan: Wuhan University of Technology
Erscheinungsjahr
2018
Quelle
SpringerLink
Beschreibungen/Notizen
The sintering of chromium-containing vanadium-titanium magnetite using different coke contents was studied through the sintering pot tests, X-ray diffraction analysis and mineralogical phase analysis. Results showed that, as the coke content increased from 3.2% to 4.4%, the liquid phase and combustion zone thickness increased while the vertical sintering rate and ratio of sintered product decreased. In addition, the combustion ratio of exhaust gas also increased with increasing the coke content, indicating that combustion zone temperature also increased, and the excessive the coke content in the sintering process of vanadiumtitanium magnetite is harmful. As the coke content increased, the magnetite, silicates, and perovskite contents of the sintered ore increased while the contents of hematite and calcium ferrite of sintered ore decreased; drum strength decreased, and reduction degradation properties increased while reduction ability decreased. We found that the appropriate coke content for the sintering process is 3.6 wt%.