Details

Autor(en) / Beteiligte

• Mundy, J. Zachary
• Shafiefarhood, Arya
• Li, Fanxing
• Khan, Saad A.
• Parsons, Gregory N.

Titel

Low temperature platinum atomic layer deposition on nylon-6 for highly conductive and catalytic fiber mats

Ist Teil von

• Journal of vacuum science & technology. A, Vacuum, surfaces, and films, 2016-01, Vol.34 (1)

Ort / Verlag

United States

Erscheinungsjahr

2016

Quelle

American Institute of Physics (AIP) Journals

Beschreibungen/Notizen

• Low temperature platinum atomic layer deposition (Pt-ALD) via (methylcyclopentadienyl)trimethyl platinum and ozone (O3) is used to produce highly conductive nonwoven nylon-6 (polyamide-6, PA-6) fiber mats, having effective conductivities as high as ∼5500–6000 S/cm with only a 6% fractional increase in mass. The authors show that an alumina ALD nucleation layer deposited at high temperature is required to promote Pt film nucleation and growth on the polymeric substrate. Fractional mass gain scales linearly with Pt-ALD cycle number while effective conductivity exhibits a nonlinear trend with cycle number, corresponding to film coalescence. Field-emission scanning electron microscopy reveals island growth mode of the Pt film at low cycle number with a coalesced film observed after 200 cycles. The metallic coating also exhibits exceptional resistance to mechanical flexing, maintaining up to 93% of unstressed conductivity after bending around cylinders with radii as small as 0.3 cm. Catalytic activity of the as-deposited Pt film is demonstrated via carbon monoxide oxidation to carbon dioxide. This novel low temperature processing allows for the inclusion of highly conductive catalytic material on a number of temperature-sensitive substrates with minimal mass gain for use in such areas as smart textiles and flexible electronics.