High‐entropy boride–carbide ceramics by sequential boro/carbothermal synthesis
Ist Teil von
Journal of the American Ceramic Society, 2022-09, Vol.105 (9), p.5543-5547
Ort / Verlag
Columbus: Wiley Subscription Services, Inc
Erscheinungsjahr
2022
Quelle
Wiley Online Library Journals Frontfile Complete
Beschreibungen/Notizen
A dual‐phase high‐entropy boride (HEB)/carbide (HEC) ceramic with a fine grain size was synthesized by a sequential boro/carbothermal process. In the first step, an Hf–Nb–Ta–Ti–Zr‐containing carbide was synthesized by a carbothermal reduction of oxides followed by the reaction of the carbide with B4C and ZrH2 to convert part of the carbide to boride. The resulting composition was ∼29 vol% HEB with an average grain size of ∼1.1 μm. Solid solution formation occurred at the densification temperature of 1900°C resulting in a relative density higher than 99%. The Vickers hardness was 26.5 ± 1.4 GPa. This is the first report of synthesizing dual‐phase boride–carbide high‐entropy ceramics from carbothermally synthesized, HEC powders.