UNIVERSI
TÄ
TS-
BIBLIOTHEK
P
ADERBORN
Anmelden
Menü
Menü
Start
Hilfe
Blog
Weitere Dienste
Neuerwerbungslisten
Fachsystematik Bücher
Erwerbungsvorschlag
Bestellung aus dem Magazin
Fernleihe
Einstellungen
Sprache
Deutsch
Deutsch
Englisch
Farbschema
Hell
Dunkel
Automatisch
Sie befinden Sich nicht im Netzwerk der Universität Paderborn. Der Zugriff auf elektronische Ressourcen ist
gegebenenfalls
nur via VPN oder Shibboleth (DFN-AAI) möglich.
mehr Informationen...
Universitätsbibliothek
Katalog
Suche
Details
Zur Ergebnisliste
Ergebnis 4 von 106
Datensatz exportieren als...
BibTeX
Optimization of thermopressing conditions for the production of binderless boards from a coriander twin‐screw extrusion cake
Journal of applied polymer science, 2017-04, Vol.134 (13), p.np-n/a
Uitterhaegen, E.
Labonne, L.
Merah, O.
Talou, T.
Ballas, S.
Véronèse, T.
Evon, Ph
2017
Volltextzugriff (PDF)
Details
Autor(en) / Beteiligte
Uitterhaegen, E.
Labonne, L.
Merah, O.
Talou, T.
Ballas, S.
Véronèse, T.
Evon, Ph
Titel
Optimization of thermopressing conditions for the production of binderless boards from a coriander twin‐screw extrusion cake
Ist Teil von
Journal of applied polymer science, 2017-04, Vol.134 (13), p.np-n/a
Ort / Verlag
Hoboken: Wiley Subscription Services, Inc
Erscheinungsjahr
2017
Quelle
Wiley Online Library Journals Frontfile Complete
Beschreibungen/Notizen
ABSTRACT A deoiled press cake resulting from twin‐screw extrusion of coriander fruits was used as a raw material for the production of self‐bonded boards. The operating parameters for thermopressing were varied and include the applied pressure (19.6–39.2 MPa), molding time (60–300 s), and molding temperature (155–205 °C). The optimized process conditions (21.6 MPa, 300 s, 205 °C) resulted in a board with a density of 1323 kg/m3, a flexural strength of 23 MPa, a modulus of elasticity of 4.4 GPa, and a thickness swelling of 31%. The thickness swelling was effectively reduced to 20% through the application of a heat treatment at 200 °C after thermopressing. A variation of the moisture content of the press cake between 3 and 8% showed that increased moisture contents do not lead to improved mechanical properties of the resulting board and further induce internal fracturing of the board during thermopressing. The manufactured binderless boards may act as environmentally friendly alternatives to commercial wood‐based boards such as oriented strand board and particleboard. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017, 134, 44650.
Sprache
Englisch
Identifikatoren
ISSN: 0021-8995
eISSN: 1097-4628
DOI: 10.1002/app.44650
Titel-ID: cdi_hal_primary_oai_HAL_hal_01416004v1
Format
–
Schlagworte
Boards
,
Cakes
,
Chemical engineering
,
Chemical Sciences
,
Materials science
,
mechanical properties
,
Mechanics
,
Modulus of rupture in bending
,
Moisture content
,
molding
,
Molding (process)
,
Physics
,
Polymers
,
Presses
,
proteins
,
Strands
,
Swelling
,
thermal properties
,
Thermics