Comparing with the traditional method to make tin oxide (SnO
2) sensor material (hydrolysis of SnCl
4 in basic solutions), a novel CVD strategy has been investigated to prepare high sensitive SnO
2 microspheres. SnCl
2 is used as the precursor to form SnS
2 microsphere, which is composed of single-crystal SnS
2 sheet. Then, the sample is oxidized in air and transformed to polycrystalline SnO
2 microsphere.
▪
Comparing with the traditional method to make the tin oxide (SnO
2) sensor material (hydrolysis of SnCl
4 in basic solutions), a novel CVD strategy has been investigated to prepare highly sensitive SnO
2 microspheres. SnCl
2 was used as the precursor to form SnS
2 microspheres, which was composed of single-crystal SnS
2 sheet. Then, the sample was oxidized in air and transformed to polycrystalline SnO
2 microspheres. BET surface area and BJH pore diameter were measured with nitrogen adsorption at 77.36
K on a Chemsorb-3000 instrument. X-ray diffraction (XRD) and transmission electron microscopy (TEM) results showed the sample had small grain size, which made it highly sensitive to ethanol.