Phase relations in the Gd2O3-Sm2O3-ZrO2 system: Experimental studies and thermodynamic modeling
Ist Teil von
Journal of alloys and compounds, 2024-09, Vol.998, p.174965, Article 174965
Ort / Verlag
Elsevier B.V
Erscheinungsjahr
2024
Quelle
Alma/SFX Local Collection
Beschreibungen/Notizen
Sm2Zr2O7 and Gd2Zr2O7 are two promising transparent ceramic materials with high density and effective atomic number. However, the phase diagram of Gd2O3-Sm2O3-ZrO2 system has not been systematically studied. To determine the phase relationship of the ternary system Gd2O3-Sm2O3-ZrO2 at 1600°C and 1400°C, a serious of ceramic samples were prepared and studied by X-ray diffraction, scanning electron microscope, and electron probe microanalysis. In the range of 66.6 mol.% ZrO2, the solubility of Gd2O3 is 20–22.5 mol.% at 1600°C, and the binary intermediate phases Sm2Zr2O7 and Gd2Zr2O7 form a continuous solid solution at 1400°C. Using the experimental data as a foundation, thermodynamic modeling was performed using the approach. Based on the experimental data, the mixing parameters of fluorite, B and C phases were optimized, and thermodynamic modeling was performed using the CALPHAD (CALculation of PHAse Diagram) method. For the first time, a self-consistent database for Gd2O3-Sm2O3-ZrO2 ternary system was established.
•Phase equilibria of Gd2O3-Sm2O3-ZrO2 system were studied experimentally at 1600°C and 1400°C.•At 1400°C, Gd2Zr2O7 and Sm2Zr2O7 form a continuous solid solution, and at 1600°C, the solubility of Gd2O3 is 20-22.5 mol%.•A set of self-consistent thermodynamic description for the Gd2O3-Sm2O3-ZrO2 system was established for the first time.