Titel

Drastic Ce3+ Insertion Enhancement in YAG Garnet Nanocrystals Through a Solvothermal Route

Ist Teil von

• Frontiers in materials, 2021-11, Vol.8

Ort / Verlag

Frontiers Media S.A

Erscheinungsjahr

2021

Link zum Volltext

Quelle

EZB Electronic Journals Library

Beschreibungen/Notizen

• Y 3 Al 5 O 12 (YAG) nanocrystals have been synthesized by a modified solvothermal method (300°C) allowing the incorporation of cerium ions in much larger proportion (up to 30 mol.% with respect to yttrium ions) than ever published. The reasons are the nanometric size of the produced nanocrystals, allowing to accommodate Ce 3+ ions in the rigid YAG structure thanks to the presence of local distortions, and also the soft synthesis route, at low temperatures and far from the thermodynamic equilibrium, which favors the cerium insertion. As a consequence, Ce 3+ photoluminescence spectrum can be tuned with the doping concentration, from 541 nm for low Ce 3+ concentration to 580 nm for a cerium concentration of 30 mol.%. The internal quantum yield reaches 40 ± 5% before decreasing due to concentration quenching. The nanocrystal brightness, which combines the internal quantum yield and the cerium concentration, has been found optimal for a doping of 2 mol.% Ce 3+ .