Titel

Design, Metallurgical Features, and Mechanical Behaviour of NiTi Endodontic Instruments from Five Different Heat-Treated Rotary Systems

Ist Teil von

• Materials, 2022-01, Vol.15 (3), p.1009

Ort / Verlag

Switzerland: MDPI AG

Erscheinungsjahr

2022

Quelle

EZB Electronic Journals Library

Beschreibungen/Notizen

• The current study aimed to compare the F1 endodontic instruments from five different heat-treated rotary systems regarding their design, metallurgical properties, and mechanical performance. Five F1 root canal shaping instruments (ProTaper Gold [PTG], Premium Taper Gold, Go-Taper Flex, EdgeTaper Platinum, and Super Files Blue)-plus, a conventional ProTaper Universal (PTU)-which were evaluated regarding their design, nickel/titanium ratio, phase transformation temperatures, microhardness, cyclic fatigue, and torsional and bending strengths. Mood's median test was used for the statistical comparison with a significance set at 5%. The instruments were similar regarding the nickel/titanium ratio and overall design. Go-Taper Flex had the closest transformation temperatures to PTG. PTU and Go-Taper Flex had the highest microhardness (408.3 and 410.5 HVN). The time to fracture of Super Files Blue was three and seven times higher than PTG and PTU, respectively. No difference was observed in the maximum torque to fracture among PTG (1.30 N·cm) and the other systems, except for the Premium Taper Gold (1.05 N·cm) and Go-Taper Flex (1.10 N·cm). Significantly lower bending loads than PTG (269.2 gf) were observed for the EdgeTaper Platinum (158.3 gf) and Premium Taper Gold (103.5 gf) instruments. Super Files Blue outperformed PTG in the cyclic fatigue test, while EdgeTaper Platinum and Premium Taper Gold were more flexible. Premium Taper Gold and Go-Taper Flex showed lower torsional strength.