Nitridated Ca2NaMg2V3O12: Eu3+ Vanadate Garnet Phosphor-in-Glass

Ist Teil von

• Materials, 2020-07, Vol.13 (13), p.2996

Ort / Verlag

Basel: MDPI AG

Erscheinungsjahr

2020

Quelle

Free E-Journal (出版社公開部分のみ）

Beschreibungen/Notizen

• In this study, Ca2NaMg2V3O12 coordination compound undoped and doped with Eu3+ obtained in the air and ammonia atmosphere by solid-state reaction was investigated. Ca2NaMg2V3O12: Eu3+ obtained in the ammonia atmosphere was then investigated as a phosphor-in-glass (PiG). Annealed Ca2NaMg2V3O12: Eu3+ phosphor forms a single phase with the cubic garnet structure and Ia3d space group. Nitridation in ammonia causes a widening of a VO43− group emission band on the low energy side and it red-shifts by 20 nm. The emission of Eu3+ is extended as compared to the non-nitridated phosphor. Ca2NaMg2V3O12: Eu3+ after nitridation shows higher emission quantum yield (QY): 49 vs. 45 and lower correlated color temperature (CCT) and 4179 vs. 4998 as compared to phosphor without nitridation. The QY for PiG is 55. The thermal stability of nitridated phosphors is superior to phosphor obtained in the air atmosphere and is further enhanced for PiG.