Details

Autor(en) / Beteiligte

• Zhao, Yixuan
• Song, Yuqing
• Hu, Zhaoning
• Wang, Wendong
• Chang, Zhenghua
• Zhang, Yan
• Lu, Qi
• Wu, Haotian
• Liao, Junhao
• Zou, Wentao
• Gao, Xin
• Jia, Kaicheng
• Zhuo, La
• Hu, Jingyi
• Xie, Qin
• Zhang, Rui
• Wang, Xiaorui
• Sun, Luzhao
• Li, Fangfang
• Zheng, Liming
• Wang, Ming
• Yang, Jiawei
• Mao, Boyang
• Fang, Tiantian
• Wang, Fuyi
• Zhong, Haotian
• Liu, Wenlin
• Yan, Rui
• Yin, Jianbo
• Zhang, Yanfeng
• Wei, Yujie
• Peng, Hailin
• Lin, Li
• Liu, Zhongfan

Titel

Large-area transfer of two-dimensional materials free of cracks, contamination and wrinkles via controllable conformal contact

Ist Teil von

• Nature communications, 2022-07, Vol.13 (1), p.4409-4409, Article 4409

Ort / Verlag

London: Nature Publishing Group

Erscheinungsjahr

2022

Link zum Volltext

Quelle

Alma/SFX Local Collection

Beschreibungen/Notizen

• Abstract The availability of graphene and other two-dimensional (2D) materials on a wide range of substrates forms the basis for large-area applications, such as graphene integration with silicon-based technologies, which requires graphene on silicon with outperforming carrier mobilities. However, 2D materials were only produced on limited archetypal substrates by chemical vapor deposition approaches. Reliable after-growth transfer techniques, that do not produce cracks, contamination, and wrinkles, are critical for layering 2D materials onto arbitrary substrates. Here we show that, by incorporating oxhydryl groups-containing volatile molecules, the supporting films can be deformed under heat to achieve a controllable conformal contact, enabling the large-area transfer of 2D films without cracks, contamination, and wrinkles. The resulting conformity with enhanced adhesion facilitates the direct delamination of supporting films from graphene, providing ultraclean surfaces and carrier mobilities up to 1,420,000 cm 2 V −1 s −1 at 4 K.