Effects of High-Intensity Ultrasound on the Microstructure and Mechanical Properties of 2195 Aluminum Ingots

Ist Teil von

• Metals (Basel ), 2021-07, Vol.11 (7), p.1050

Ort / Verlag

Basel: MDPI AG

Erscheinungsjahr

2021

Link zum Volltext

Quelle

EZB Electronic Journals Library

Beschreibungen/Notizen

• The microstructural refinement of 2195 aluminum alloy ingots is particularly important for improving their industrial applications and mechanical properties. Combined with vacuum casting and inert gas protection, scalable high-strength ultrasonic melt processing (USMT) technology was used to manufacture 2195 aluminum alloy cylindrical ingots. Then, the influence of USMT on the main microstructural components (primary α-Al grains, secondary phase network, and precipitated particles) was studied. Our experiments show that the main microstructure of the ingot was improved after the introduction of ultrasound. Compared to the ingot formed without USMT, the size and morphology of the primary α-Al phase were optimized. The agglomeration of coarsening secondary phases can be alleviated, and the large layered secondary phase network becomes discontinuous throughout the ingot under USMT. At the same time, the mechanical properties of the solidified aluminum alloy ingots were also tested, and comparisons were made between samples formed with and without USMT. The results show that the stress concentration caused by the large area of coarse secondary phase in the ingot leads to the decrease of mechanical properties.