Morphological and Structural Transformations of Fe-Pd Powder Alloys Formed by Galvanic Replacement, Annealing and Acid Treatment

Ist Teil von

• Materials, 2022-05, Vol.15 (10), p.3571

Ort / Verlag

Switzerland: MDPI AG

Erscheinungsjahr

2022

Link zum Volltext

Quelle

EZB Electronic Journals Library

Beschreibungen/Notizen

• In this article, we report the preparation and structural features of Fe-Pd powder alloys formed by galvanic replacement, annealing and selective dissolution of iron via acid treatment. The alloys were studied by the X-ray diffraction phase analysis, Mössbauer spectroscopy, scanning electron microscopy, and energy-dispersive spectroscopy. The Fe@Pd core-shell particles were obtained by a galvanic replacement reaction occurring upon treatment of a body-centered cubic (bcc) iron powder by a solution containing PdCl ions. It was found that the shells are a face-centered cubic (fcc) Pd(Fe) solid solution. HCl acid treatment of the Fe@Pd core-shell particles resulted in the formation of hollow Pd-based particles, as the bcc phase was selectively dissolved from the cores. Annealing of the Fe@Pd core-shell particles at 800 °C led to the formation of fcc Fe-Pd solid solution. Acid treatment of the Fe-Pd alloys formed by annealing of the core-shell particles allowed selectively dissolving iron from the bcc Fe-based phase (Fe(Pd) solid solution), while the fcc Fe-rich Fe-Pd solid solution remained stable (resistant to acid corrosion). It was demonstrated that the phase composition and the Fe/Pd ratio in the alloys (phases) can be tailored by applying annealing and/or acid treatment to the as-synthesized Fe@Pd core-shell particles.