Sie befinden Sich nicht im Netzwerk der Universität Paderborn. Der Zugriff auf elektronische Ressourcen ist gegebenenfalls nur via VPN oder Shibboleth (DFN-AAI) möglich. mehr Informationen...
The Effect of Electropulsing Treatment on Properties of Pre-compressed AZ31 Magnesium Alloy
Ist Teil von
Materials research (São Carlos, São Paulo, Brazil), 2019-01, Vol.22 (6)
Ort / Verlag
ABM, ABC, ABPol
Erscheinungsjahr
2019
Quelle
EZB Electronic Journals Library
Beschreibungen/Notizen
The effect of electropulsing treatment (EPT) on quasi-static compression behavior and anisotropy of AZ31 Mg alloy were investigated based on quasi-static compression test. The results show that the orientation of the sample has a significant effect on the deformation mechanism of metal and this mechanism can be changed by pre-deformation and EPT. However, the strain rate sensitivity of the material is not affected by pre-deformation. Compared with the as-received plates, the anisotropy of AZ31 Mg alloy increased in ND-RD plane after pre-compression along the transverse direction, the ∆YS of specimens increased from 87 MPa to 98 MPa. After EPT, the anisotropy of AZ31 Mg alloy gradually decreased with the change of EPT temperature and EPT time, the ∆YS of the sample reached 14.2 MPa when EPT conducted at 200 ℃ for 15 min, which decreased 72.8 MPa compared with the as-received plates.