• Liu, Mingwei
• Wu, Fayou
• Abi, Erdi
• Wu, Linjian
• Su, Guangquan

Titel

Strength Degradation Characteristics of the Steel-Concrete Interface Under Cyclic Shear

Ist Teil von

• Tehnički vjesnik, 2022-08, Vol.29 (4), p.1372-1381

Ort / Verlag

Slavonski Baod: University of Osijek

Erscheinungsjahr

2022

Link zum Volltext

Quelle

EZB Electronic Journals Library

Beschreibungen/Notizen

• The shear capacity of the steel-concrete interface (SCI) of concrete-filled steel tubular piles (CFSTs) degrades due to the cyclic shear action of external loading and unloading and can result in a reduction in the bearing capacity. To explore the shear strength degradation characteristics of the steel-concrete interface under cyclic shear, cyclic shear tests for three roughness types and under four different normal stresses were carried out by using a large-scale repeated direct shear test system. The characteristics of the shear load-displacement curve and failure mode of the SCI under external cyclic shear were analyzed, and the influence of the roughness and normal stress on the SCI shear strength degradation was explored. The results indicate that the CFSTs experienced shear failure in the first three shear cycles and then exhibited wear failure. The peak shear load of the SCI increases exponentially with increasing normal stress and decreases logarithmically with increasing cyclic shear time. A larger interfacial roughness and normal stress results in a faster interfacial shear strength ratio (THAH) weakening during the first three shear cycles, and with an increase of the cyclic shear times, the weakening rate is reduced.