• Murakami, Taichi
• Maruoka, Daisuke
• Kasai, Eiki

Titel

Effect of Silica in Ash of Coke on Carburization and Melting of Iron

Ist Teil von

• ISIJ International, 2021/05/15, Vol.61(5), pp.1479-1487

Ort / Verlag

The Iron and Steel Institute of Japan

Erscheinungsjahr

2021

Quelle

EZB Electronic Journals Library

Beschreibungen/Notizen

• Reducing energy consumption in ironmaking process is essential for decreasing the amount of carbon dioxide emission from the blast furnace process. To effectively reduce carbon dioxide emission, a faster reduction of iron ore, as well as the acceleration of carburization and melting of the reduced iron is important. Understanding the ash behavior of coke in blast furnace is necessary for controlling carburization because ash prevents carburization. In this study, the following were investigated:1) Condensation behavior of the ash components on the surface of coke by gasification under the simulated blast furnace condition2) Melting behavior of iron tablet by the direct contact with coke plate3) In-situ observation of the melting behavior of coke-iron composite and effect of deashing treatment4) In-situ observation of the melting behavior of Fe–Si alloy using graphiteThe results revealed that ash condenses on the coke surface via gasification, and the ash coverage ratio of the coke surface increases with increasing in the coke reactivity. In addition, the melting of iron by carburization with coke proceeds at lower temperature when the coke reactivity is high. However, the effect of ash coverage on this behavior is significantly higher than that of coke reactivity, and an increase in the ash coverage ratio suppresses the carburization and melting of iron. In addition, during holding at high temperature, SiO2 in ash is reduced to Si, and it alloys with metallic iron. Furthermore, an increase in Si concentration in metallic iron increases the melting temperature of Fe–Si system. Consequently, carburization and melting iron are suppressed.