Near-complete blocking of multivalent anions in graphene oxide membranes with tunable interlayer spacing from 3.7 to 8.0 angstrom
Ist Teil von
Journal of membrane science, 2019-12, Vol.592, p.117394, Article 117394
Ort / Verlag
Elsevier B.V
Erscheinungsjahr
2019
Quelle
Access via ScienceDirect (Elsevier)
Beschreibungen/Notizen
Graphene oxide (GO) membranes have attracted attention as a promising candidate for selective ion permeation due to narrow interlayer spacing. Among several methods to control the interlayer spacing, the reduction of GO membranes has great potential for desalination and water purification. To apply GO membranes for ion separation, investigating ion transport of sub-nanometer channels of reduced GO membranes is needed. In this study, thermally and chemically reduced GO membranes were fabricated with different interlayer spacing ranging from 3.7 to 8.0 Å in a dry state. It was experimentally determined that the minimum spacing allowing water permeation was 5.7 Å (9.6 Å in water), and no water permeated at 5.0 Å or less. For ion permeation, a pure GO membrane exhibited similar permeability for most ions, while the permeability of GO membrane with 5.7 Å spacing was strongly dependent of the size and charge of ions. The permeability of cations significantly changed along with the ionic radius, while there was a noticeable cutoff for permeability of multivalent anions such as SO42− and Fe(CN)63−. Our reduced GO membrane could be used to effectively block the permeation of large ions and multivalent anions.
•Thermally-reduced graphene oxide (GO) membranes for tuning an interlayer spacing.•Precise control of the interlayer spacing from 3.7 to 8.0 Å in a dry state.•Sieving of multivalent anions in a 9.6 Å (in water) GO membrane.•Finding minimum allowable spacing of GO membrane to permeate water molecules.•Explaining sieving mechanism for positive and negative ions with different size.