• Li, Jianqiang
• Bai, Songwei
• Liu, Heyan
• Luo, Hongzhi
• Meng, Fanbin

Titel

Effect of B substitution for Si on the electronic structure and magnetic properties of Heusler alloys Fe2CoSi1-xBx (x = 0–0.25)

Ist Teil von

• Journal of magnetism and magnetic materials, 2022-12, Vol.564, p.170090, Article 170090

Ort / Verlag

Elsevier B.V

Erscheinungsjahr

2022

Quelle

Alma/SFX Local Collection

Beschreibungen/Notizen

• •Melt-spinning can help to reduce precipitation of the secondary phase and form a highly ordered structure in Heusler alloys Fe2CoSi1-xBx (x = 0–0.25)•B atoms mainly enter the substitutional site in Fe2CoSi1-xBx and single Heusler phase can be obtained when ×  = 0–0.10.•Fe2CoSi1-xBx Heusler alloys are candidates for spintronic applications within the range of ×  = 0–0.1.•Deviation between the Ms at 5 K and calculated total spin moment is observed when B content is high, resulting from the Fe2B-type secondary phase. A series of Fe2CoSi1-xBx (x = 0, 0.05, 0.1, 0.15, 0.2 and 0.25) Heusler alloys has been synthesized using melt-spinning method, which can help to reduce the precipitation of the secondary phase and form a highly ordered structure. The XRD patterns indicate that, when x  = 0–0.1 the Fe2CoSi1-xBx melt-spun ribbons are single Heusler phases, but when x  = 0.2 and 0.25 a small amount of secondary phase appears. The lattice constant decreases with increasing B content, suggesting that B mainly enters the substitutional sites of Si. The Curie temperatures TC of Fe2CoSi1-xBx alloys are all higher than 1000 K, and a 21 K increase of TC is observed as x varies from 0 to 0.25. The hysteresis loops of Fe2CoSi1-xBx alloys show soft magnetic character. Their saturation magnetizations Ms at 5 K and 300 K are similar and close to 5μB / f.u. The zero-gap half-metallic character reported for Fe2CoSi has been confirmed in present work. But with the substitution of B for Si, the Fermi level moves from the center in Fe2CoSi DOS to the left edge of the minority energy gap in Fe2CoSi0.75B0.25, which may disturb the half-metallic character when B content is high. When ×  = 0–0.1, the Ms at 5 K of Fe2CoSi1-xBx agree well with the calculated total spin moments, but when the B content is high, especially when x  = 0.2 and 0.25, a deviation between the experimental and theoretical results is observed, which is related to the secondary phase in these samples.