Elucidation of cold-spray deposition mechanism by auger electron spectroscopic evaluation of bonding interface oxide film
Ist Teil von
Acta materialia, 2019-02, Vol.164, p.39-49
Ort / Verlag
Elsevier Ltd
Erscheinungsjahr
2019
Link zum Volltext
Quelle
Alma/SFX Local Collection
Beschreibungen/Notizen
The relationship between the cold spray deposition mechanism, microstructure, and strength of the resulting film must be understood for this innovative process to be practical. Previous studies have suggested that the coating mechanism is reliant on breaking the natural oxide film such that metallic bonding occurs through direct contact between the metal surfaces. In this study, the proposed model was experimentally verified by a small tensile adhesion test and auger electron spectroscopy analysis of the bonding interface. Since shear deformation does not occur at the tip (south pole) of the incoming particle, the oxide film is not broken, such that the bonding strength is weak. In contrast, at the outer edge of the particle, metallic bonding occurs, attaining a level of strength that exceeds that of the base material due to the huge plastic deformation. This phenomenon is known as the “south-pole problem,” and can lead to a decrease in the overall adhesion strength despite the local adhesion being strong. However, detailed observations revealed, in parts of the deposits, particles that had adhered across their entire surface. This suggests that, provided the collision state can be controlled, it is possible to overcome the south-pole problem and improve the adhesion strength.
[Display omitted]