Details

Autor(en) / Beteiligte

• Zhang, Dazheng
• Gao, Xiuhua
• Su, Guanqiao
• Du, Linxiu
• Liu, Zhenguang
• Hu, Jun

Titel

Corrosion Behavior of Low-C Medium-Mn Steel in Simulated Marine Immersion and Splash Zone Environment

Ist Teil von

• Journal of materials engineering and performance, 2017-06, Vol.26 (6), p.2599-2607

Ort / Verlag

New York: Springer US

Erscheinungsjahr

2017

Link zum Volltext

Quelle

SpringerLink (Online service)

Beschreibungen/Notizen

• The corrosion behavior of low-C medium-Mn steel in simulated marine immersion and splash zone environment was studied by static immersion corrosion experiment and wet-dry cyclic corrosion experiment, respectively. Corrosion rate, corrosion products, surface morphology, cross-sectional morphology, elemental distribution, potentiodynamic polarization curves and electrochemical impedance spectra were used to elucidate the corrosion behavior of low-C medium-Mn steel. The results show that corrosion rate in immersion zone is much less than that in splash zone owing to its relatively mild environment. Manganese compounds are detected in the corrosion products and only appeared in splash zone environment, which can deteriorate the protective effect of rust layer. With the extension of exposure time, corrosion products are gradually transformed into dense and thick corrosion rust from the loose and porous one in these two environments. But in splash zone environment, alloying elements of Mn appear significant enrichment in the rust layer, which decrease the corrosion resistance of the steel.